On the relation between micro and macroscopic fatigue crack growth rates in aluminum alloy AMS 7475-T7351 (2006)
- Autores:
- Autores USP: TARPANI, JOSÉ RICARDO - EESC ; BOSE FILHO, WALDEK WLADIMIR - EESC ; SPINELLI, DIRCEU - EESC
- Unidade: EESC
- DOI: 10.1007/s10704-006-9029-2
- Assuntos: LIGAS NÃO FERROSAS; FADIGA DOS MATERIAIS
- Idioma: Inglês
- Imprenta:
- Fonte:
- Título do periódico: International Journal of Fracture
- ISSN: 0376-9429
- Volume/Número/Paginação/Ano: v. 142, n. 3/4, p. 233-240, Dec. 2006
- Este periódico é de assinatura
- Este artigo NÃO é de acesso aberto
- Cor do Acesso Aberto: closed
-
ABNT
RUCKERT, Cassius Olívio Figueiredo Terra et al. On the relation between micro and macroscopic fatigue crack growth rates in aluminum alloy AMS 7475-T7351. International Journal of Fracture, v. 142, n. 3/4, p. 233-240, 2006Tradução . . Disponível em: https://doi.org/10.1007/s10704-006-9029-2. Acesso em: 19 abr. 2024. -
APA
Ruckert, C. O. F. T., Tarpani, J. R., Bose Filho, W. W., & Spinelli, D. (2006). On the relation between micro and macroscopic fatigue crack growth rates in aluminum alloy AMS 7475-T7351. International Journal of Fracture, 142( 3/4), 233-240. doi:10.1007/s10704-006-9029-2 -
NLM
Ruckert COFT, Tarpani JR, Bose Filho WW, Spinelli D. On the relation between micro and macroscopic fatigue crack growth rates in aluminum alloy AMS 7475-T7351 [Internet]. International Journal of Fracture. 2006 ; 142( 3/4): 233-240.[citado 2024 abr. 19 ] Available from: https://doi.org/10.1007/s10704-006-9029-2 -
Vancouver
Ruckert COFT, Tarpani JR, Bose Filho WW, Spinelli D. On the relation between micro and macroscopic fatigue crack growth rates in aluminum alloy AMS 7475-T7351 [Internet]. International Journal of Fracture. 2006 ; 142( 3/4): 233-240.[citado 2024 abr. 19 ] Available from: https://doi.org/10.1007/s10704-006-9029-2 - Estimating fatigue life under variable amplitude loading through quantitative fractography: a case study
- Load ratio estimative through height and interstriation spacing analysis of an aeronautical alloy SAE AMS 7475-T7351
- Resistência ao impacto de compósitos derivados da biomassa: sisal/poliuretano e coco/poliuretano
- Mechanical performance of carbon-epoxy laminates part II: quasi-static and fatigue tensile properties
- Evaluating the Berkovitz method to predict fatigue loads in mechanical failure investigations
- High temperature fatigue properties of pearlitic gray cast irons employed in brake discs
- Fatigue in riveted lap joints of fiber-metal laminate glare
- Evaluating the Berkovitz's k-parametrization method to predict fatigue loads in failure investigations
- Catastrophic failure of a rotating forged flange in a brazilian sugarcane mill
- Estimating fatigue life under variable amplitude loading through quantitative fractography: a case study
Informações sobre o DOI: 10.1007/s10704-006-9029-2 (Fonte: oaDOI API)
Como citar
A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas